Plastics Decorating

LATEST ISSUE


VIEW THE ONLINE EDITION

Profile
High-Tech Contract Decorating at Emerald Corporation

Show Preview
2012 SGIA Expo Show Preview

Ask the Expert
Plastics Surface Energy Wetting Test Methods

Technology
Scratch-resistant in One Step

Association
Letter from the Chair
TopCon Rolls Through Indy
Digital Decorating Webinar Scheduled for August 28

Assembly
Ultrasonic Welding: The Need for Speed Control

Management
How to Close Sales that are Over the Budget


CALENDAR

February 12-14
PLASTEC West, Anaheim Convention Center, Anaheim, CA, www.plastecwest.com

March 19
Plastics Crossroads Summit, Sheraton Hotel, Anaheim, CA, www.rjginc.com/plasticscrossroads

March 20-21
PLASTEC South, Orange County Convention Center, Orlando, FL, www.plastecsouth.com

April 8
AWA DecTec USA, Orange County Convention Center, Orlando, FL, www.awa-bv.com

April 22-24
SPE ANTEC® 2013, Duke Energy Convention Center, Cincinnati, OH, www.antec.ws

June 18-20
HBA, June 18-20, Jacob K. Javits Convention Center, New York City, NY, www.hbaexpo.com

June 18-20
PLASTEC East, , Pennsylvania Convention Center, Philadelphia, PA, www.plasteceast.com


Omnexus
Source IML IMDA

   
Join Our Email List
Email:  
   
For Email Marketing you can trust

 

Copyright 2010 Peterson Publications, Inc.

Plastics Decorating Magazine 
2150 SW Westport Dr., Suite 101 
Topeka, KS 66614 
(785) 271-5801Ā  Fax (785) 271-6404

 


Eco-Friendly Waterborne Coatings

 

By Scott Sabreen, The Sabreen Group, Inc.

Decorative waterborne coatings are environmentally-friendly and provide exceptional appearance and functionality. For many applications, waterborne chemistries offer equal to or better cosmetic and physical performance properties than solventborne. The advantages of waterborne coatings include high-gloss retention, scratch-resistance, high dry film thickness and ease-of-use.

Waterborne coatings are available in different curing mechanisms, including evaporation, oven bake and UV-curable. Most coatings that qualify as waterborne coatings contain some organic co-solvents in the fluidizing media. These tend to be low-molecular weight polar ketones, alcohols and esters. Typical chemical composition is approximately 50 percent water, 45 percent solids and 5 percent co-solvents (can range from 2-20 percent of the fluidizing medium). Conversely with solventborne coatings, the fluidizing medium is an organic solvent or blend of organic solvents such as MEK, MIBK, xylene, toluene, etc. All of the various spray and dip coating methods can be utilized, including air atomization, HVLP, airless and air-assisted airless. This gives waterborne processes an advantage over high-solid paints that cannot be dip coated, due to their higher viscosities. Spray guns can be cleaned with water or water-based solutions rather than paint thinner or acetone.

For drying single-component waterborne coatings, the water and co-solvents are removed from the surface of the paint coating via evaporation (physical drying or baking, without chemical cross-linking). The water below the surface migrates to the surface at a speed based upon the rate of diffusion of the coating. This process continues until all of the water has risen to the surface and is evaporated. The time in which the water is evaporated and the coating is dry is based upon the amount of water to be removed (i.e. thickness of coating and percentage of water in the paint) and the evaporation rate. The evaporation rate is dependent upon the vapor pressure difference between the water in the coating and the air being circulated over the surface of the part. The vapor pressure difference is a function of the humidity ratio (i.e. temperature and relative humidity of the circulating air) and to a smaller degree, the velocity of the air across the substrate.

Drying Considerations

The curing time for waterborne coatings is much longer than their solventborne counterparts. Adequate flash-off time between the spray booth and oven is necessary when force drying or baking the coating, otherwise solvent popping may result. It also is necessary to ensure that the surface temperature of the part is greater than the dew point to prevent condensation from forming. While this is generally not a problem during warmer months, it can be a concern during colder months. Warmer weather when the humidity is high can extend flash-off and dry times. If the humidity is high, the water vapor released during drying has no place to go, and the film will not cure. By providing moderate air flow and increased temperature, a continuous supply of fresh air can be provided to the coating to give the air more capacity to hold moisture. All water must be removed from the coating before parts are exposed to freezing temperatures. Failure to do so may result in a loss of adhesion, as the remaining water will expand upon freezing. A common mispractice of curing waterborne coatings when issues arise is to simply increase temperature and airflow velocity. Re-circulating "humid" air during curing actually decreases the vapor pressure differential and increases cure time.

Preventing Paint Failures

Many waterborne and solventborne coating failures result from inadequate surface preparation. These include both cosmetic defects and performance defects. The degree of cleanliness and higher surface energy required for waterborne coatings is greater than that necessary for most solventborne coatings due to the low solvent content. Solventborne coatings are more forgiving of residue because the solvents contained in the coatings may dissolve some surface oils and contaminates. Even though waterborne coatings typically contain "co-solvents," they still contain much less organic solvent than solventborne coatings.

Scott Sabreen is the founder and president of The Sabreen Group, Inc., a plastics engineering consulting firm. He is a board member for the Society of Plastics Engineers Decorating/Assembly Division, technical editor for Plastics Decorating and expert engineer for Omnexus/SpecialChem, Intota-Guideline and Nerac. Sabreen may be reached via email at ssabreen@sabreen.com.